Application of Pressure Treatment Methods for Solid Processing of Silumin Chip Waste
Published date: Dec 31 2020
Journal Title: KnE Materials Science
Issue title: IV Congress “Fundamental Research and Applied Developing of Recycling and Utilization Processes of Technogenic Formations” Volume 2020
Pages: 560–566
Authors:
Abstract:
n this article various technological schemes for processing waste in the form of chips of an alloy of an aluminum-silicon system are presented. It was noted that the processing of fine waste of the chips type is always accompanied by oxidation of the metal due to the large surface of contact with the air. To eliminate the loss of metal into oxides during re-melting, this study proposes processing chips by pressing to obtain briquettes (a method of hot extrusion is meant by ‘pressing’). Processing involves the receipt of briquettes from rods. The processes of cold and hot briquetting were undertaken separately. The results of applying the scheme using real production waste are presented in this study. The tensile strength achieved was up to 270 MPa. The relative elongation to rupture was 10–25% and the area reduction after rupture was 25–45%. There were no large differences in the use of briquettes obtained by cold processing and hot processing. The conclusion is drawn about the overall effectiveness of the application of the waste processing without the use of the metal melting.
Keywords: silumin, shavings, extrusion, plastic deformation, heat treatment
References:
[1] Ab Rahim, S. N., Lajis, M. A. and Ariffin, S. (2015). A Review on Recycling Aluminum Chips by Hot Extrusion Process. Presented at 12th Global Conference on Sustainable Manufacturing. September, 2015, Ho Chi Minh City, Vietnam. Binh Duong International Convention & Exhibition Ho Chi Minh City, Vietnam, Procedia CIRP. vol. 26, pp. 761 – 766.
[2] Shamsudin, S., Lajis, M. and Zhong, Z.W. (2016). Evolutionary in Solid State Recycling Techniques of Aluminium: A Review. Procedia CIRP, vol. 40, pp. 256-261.
[3] Chiba, R. and Yoshimura, M. (2015). Solid-state Recycling of Aluminium Alloy Swarf into c-channel by Hot Extrusion. Journal of Manufacturing Processes, vol. 17, pp. 1-8.
[4] Haase, M. and Tekkaya, A. E. (2015). Haase, M., Tekkaya and Erman. (2015). Cold Extrusion of Hot Extruded Aluminum Chips. Journal of Materials Processing Technology, vol. 217, pp. 356–367.
[5] Zagirov, N. N., et al. (2018). Alternative Technology for Manufacturing Rod–Wire Products from AK12 Silumin. Metallurgist, vol. 62(5-6), pp. 587-596.
[6] Zagirov, N. N., et al. (2017). Comparative Analysis of Technologies of Welding Wire Production from Eutectic Silumin using Combined Processing Methods. Tsvetnye Metally, vol. 4, pp. 86-92.
[7] Ershov, A. A., et al. (2016). Simulation of the Consolidation of a Porous Material in a Combined Rolling– Extrusion Process. Metallurgist, vol. 60, issue 5-6, pp. 561-565.
[8] Lela, B., Krolo, J. and Jozić, S. (2016). Mathematical Modeling of Solid-State Recycling of Aluminum Chips. International Journal of Advanced Manufacturing Technology, vol. 87, issue 1-4, pp. 1125-1133.
[9] Rady, M. H., et al. (2019). Effect of Hot Extrusion Parameters on Microhardness and Microstructure in Direct Recycling of Aluminium Chips. Materialwissenschaft und Werkstofftechnik, vol. 50, issue 6, pp. 718-723.