Published date:May 06 2018

Journal Title: KnE Material Sciences

Issue title: 15th International School-Conference "New Materials – Materials of Innovative Energy" (MIE)

Pages:534–540

DOI: 10.18502/kms.v4i1.2207

A G Zholninazholnin@list.ru

A P Melnikov

E G Grigoriev

V V Stolyarov

Dependence of specific electrical resistance on temperature (20 - 1600 ∘C) and processing method in an aluminum-graphene (up to 2wt.%) composite is investigated. It is established that spark plasma sintering (SPS) under pressure 40 MPа does not influence on electrical resistance, whereas SPS at low pressure (<10 MPa) reduces electrical resistance at a room temperature on 6 orders. Lower values of electrical resistance (up to 90 Ω *mm) received at sintering in hot pressing set at radiating heating. It is supposed that the reason of sharp decrease in electrical resistance at the lowered pressure is presence of current pulsations during SPS. They induces magnetic fields in graphene flake which lead to their moving and forming of particles to electroconductive chains or their capture in arched cells at applied pressure.

Keywords: composite, aluminum, graphene, electrical resistance, temperature dependence.

[1] Graphene-based composite materials Stankovich S. et al., Nature 442, 2006, 282.


[2] Two-dimensional gas of massless Dirac fermions in graphene. Novoselov K. S. et al., Nature 438, 2005, 197.


[3] Graphene for tough and electroconductive alumina ceramics A. Centeno, V.G. Rocha, B. Alonso, et al., Journal of the European Ceramic Society 33 (2013) 3201–3210


[4] He T, Li J, Wang L, et al. Preparation and consolidation of alumina/graphene composite powders. Mater Trans 2009;50:749–51.


[5] Kim H. J. et al. Unoxidized Graphene/Alumina Nanocomposite: Fracture and Wear Resistance Effects of Graphene on Alumina Matrix. Sci. Rep. 4, 2014, 5176.


[6] Centeno A., Rocha V.G., Alonso B., et al, Graphene for tough and electroconductive alumina ceramics. J. Eur. Ceram. Soc. 333, 2013, 201–321.


[7] Structure and properties of Al2O3 / Graphene nanocomposite processed by spark plasma sintering. V.V. Stolyarov, A. A Misochenko, A G Zholnin, et al. IOP Conf. Series: Materials Science and Engineering 218 (2017) 012017 doi:10.1088/1757- 899X/218/1/012017


[8] Spark-plasma sintering of nanocomposite Al2O3–Graphene. А.Zholnin, E. Klyatskina, E. Grigoriev, V.Stolyarov, Phisics and chemistry of treatment of materials 2017, № 4, 47-54


[9] Spark-plasma sintering of nanocomposite Al2O3–Graphene. А.Zholnin, E. Klyatskina, E. Grigoriev, V.Stolyarov, Proceedings of 10