Effect of Curing Temperature in the Alkali-Activated Brick Waste and Glass Powder mortar and Their Influence of Mechanical resistances
Published date: Apr 13 2020
Journal Title: KnE Engineering
Issue title: REMINE International Conference on Valorization of Mining and Industrial Wastes into Construction Materials By Alkali-activation
Pages: 49–61
Authors:
Abstract:
In this study, compressive strength values were measured at different curing times(7,14 and 28 days).The alkali-activation of the brick and glass powder body with potassium water glass having a silicate modulus of 3. Compressive strengths, flexural strength and specific fracture energy of the specimens stored at 40° C and 60° C are evaluated at 28-days. The study demonstrates that the storage temperature of specimens and the content of the alkaline solution have a significant influence on all mechanical properties of the studied materials.
Keywords: brick waste, glass powder, curing temperature, alkali-activated.
References:
[1] Hardjito, D., Wallah, S. E., Sumjouw, D. M. J. et al.(2003). Keynote Paper: International Conference on Recent Trends in Concrete Technology and Structures, INCONTEST, 10-11 September, Coimbatore, India.
[2] Singh, P., Sharma, S. K., Gupta, M. H. et al. (2016). Development of Geopolymer Bricks using Foundry Sand.International Research Journal of Engineering and Technology (IRJET),vol.3,issue8,pp.20452050.
[3] Si-Ahmed, M., Kenai, S. and Ghorbel, E. (2018). Performance of cement mortar with waste ground clay brick. MRS Advances, vol. 3, issue 34-35, pp. 2041-2050.
[4] Shi, C., Krivenko, P.V., and Roy, D. (2006). Alkali-activated cements and concretes. (London: Taylor & Francis).
[5] Davidovits, J. (1999). Chemistry of Geopolymeric Systems, Terminology. In Proceedings of the 99 International Conference. eds. Joseph Davidovits, R. Davidovits and C. James, (France.)
[6] Huseien, G., Ismail, M., Tahir, M., et al. (2018). Performance of sustainable alkali activated mortars containing solid waste ceramic powder. Chemical Engineering Transactions, vol. 63, pp. 673-678.
[7] Duxson, P., Provis, J. L., Lukey, G. C., et al. (2007). The role of inorganic polymer technology in the development of ‘green concrete’. Cement and Concrete Research, vol. 37, issue 12, pp. 1590-1597.
[8] Amin, S. K., El–Sherbiny, S. A., El–Magd, A. A., et al. (2017). Fabrication of geopolymer bricks using ceramic dust waste. Construction and Building Materials, vol. 157, pp. 610-620.
[9] Usha, S., Nair, D. G., and Vishnudas, S. (2016). Feasibility study of geopolymer binder from terracotta roof tile waste. Procedia Technology, vol. 25, pp. 186-193.
[10] Shi, C., Wu, Y., Riefler, C., et al. (2005). Characteristics and pozzolanic reactivity of glass powders. Cement and Concrete Research, vol. 35, issue 5, pp. 987-993.
[11] Redden,R.,andNeithalath,N.(2014).Microstructure, strength, and moisture stability of alkali-activated glass powder-based binders. Cement and Concrete Composites, vol. 45, pp. 46-56.
[12] El-Fadaly, E., Mostafa, M. R., Saraya, M. E. I., et al. (2014). Eco-friendly cement from ceramic waste geopolymarization. Natural and Social Sciences, vol. 2, issue 5, pp. 195-210.
[13] Bignozzi, M. C., Fusco, O., Fregni, A., et al. (2014). Ceramic waste as new precursors for geopolymerization. Advances in Science and Technology, vol. 92, pp. 26-31.
[14] EN, N. (2006). 196-1, Méthodes d’essais des ciments-Partie 1: détermination des résistances mécaniques. French Standard.
[15] Sethi, H., Bansal, P. P., and Sharma, R. (2019). Effect of addition of GGBS and glass powder on the properties of geopolymer concrete. Iranian Journal of Science and Technology, Transactions of Civil Engineering, vol. 43, issue 4, pp. 607-617.
[16] Hardjito, D., Cheak, C. C., and Ing, C. H. L. (2008). Strength and setting times of low calcium fly ash-based geopolymer mortar. Modern applied science, vol. 2, issue 4, pp. 3-11.
[17] Chindaprasirt, P., Chareerat, T., and Sirivivatnanon, V. (2007). Workability and strength of coarse high calcium fly ash geopolymer. Cement and concrete composites, vol. 29, issue 3, pp. 224-229.
[18] Sitarz, M., Hager, I., and Kochanek, J. (2018). Effect of High temperature on mechanical properties of geopolymer mortar. MATEC Web of Conferences, vol. 163, p. 6004.
[19] Bizzozero, J., and Scrivener, K. L. (2015). Limestone reaction in calcium aluminate cement–calcium sulfate systems. Cement and Concrete Research, vol. 76, pp. 159-169.